Changes in surface morphology of enamel after Er:YAG laser irradiation

Peter Rechmann D.D.S.; Dan S. Goldin; Thomas Hennig

doi:10.1117/12.306038

22 April 1998 Changes in surface morphology of enamel after Er:YAG laser irradiation

Peter Rechmann D.D.S., Dan S. Goldin, Thomas Hennig

Proceedings Volume 3248, Lasers in Dentistry IV; (1998) https://doi.org/10.1117/12.306038
Event: BiOS '98 International Biomedical Optics Symposium, 1998, San Jose, CA, United States

Abstract

Aim of the study was to investigate the surface and subsurface structure of enamel after irradiation with an Er:YAG laser (wavelength 2.94 micrometer, pulse duration 250 - 500 microseconds, free running, beam profile close to tophead, focus diameter 600 micrometer, focus distance 13 mm, different power settings, air-water spray 2 ml/min; KAVO Key Laser 1242, Kavo Biberach, Germany). The surface of more than 40 freshly extracted wisdom teeth were irradiated using a standardized application protocol (pulse repetition rate 4 and 6 Hz, moving speed of the irradiation table 2 mm/sec and 3 mm/sec, respectively). On each surface between 3 and 5 tracks were irradiated at different laser energies (60 - 500 mJ/pulse) while each track was irradiated between one and ten times respectively. For the scanning electron microscope investigation teeth were dried in alcohol and sputtered with gold. For light microscopic examinations following laser impact, samples were fixed in formaldehyde, dried in alcohol and embedded in acrylic resin. Investigations revealed that at subsurface level cracks can not be observed even at application of highest energies. Borders of the irradiated tracks seem to be sharp while melted areas of different sizes are observed on the bottom of the tracks depending on applied energy. Small microcracks can be seen on the surface of these melted areas.

Citation Download Citation

Peter Rechmann D.D.S., Dan S. Goldin, and Thomas Hennig "Changes in surface morphology of enamel after Er:YAG laser irradiation", Proc. SPIE 3248, Lasers in Dentistry IV, (22 April 1998); https://doi.org/10.1117/12.306038

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available