1.INTRODUCTIONAriel has been recently adopted as ESA Cosmic Vision Program M4 mission. In its 4-year nominal mission, Ariel will conduct a survey of known exoplanets to characterize their atmospheres through transit spectroscopy in the wavelength band between 0.5 μm and 8 μm. The Ariel telescope is based on an off-axis, unobscured Cassegrain design with an elliptical primary mirror with an aperture of 1100 mm (major axis) and 768 mm (minor axis) and a light collecting area of approximately 0.6 square meters. Telescope performance is diffraction limited at the wavelength of 3 μm on a 30″ Field of View. The required average telescope throughput is 96%1,2. Telescope and instruments will operate at a temperature below 50 K. Following the heritage of the JWST MIRI instrument3, aluminum alloy 6061-T651 has been chosen for mirrors substrates and supporting structures of the telescope, after a trade-off study4 on manufacturability and cost. To protect the mirrors and to improve their reflectivity in the visible section of the operating waveband, a protected silver coating with space heritage from CILAS‡ was chosen as baseline. Although several examples of cryogenic silver-coated aluminum mirrors are found in literature5–7, the large size of the primary mirror and its curvature raised concerns on the uniformity of the deposition process and stability of the coating. An initial study was therefore devised to test optical performance and durability on Al6061-T651 substrates, consisting of a qualification campaign on coated aluminum samples8, and a verification test on additional samples and on a full-scale demonstrator of Ariel primary mirror denoted PTM. This paper describes the verification tests, in particular the evaluation of coating performance and durability by means of adhesion tests, reflectivity measurements and environmental tests. 2.MATERIALS AND PROCESSES2.1Items Under TestThe coating verification tests were performed on the following items coated together in the same run: 1. the PTM (Figure 1), a spherical mirror with a radius of curvature of 2401 mm and an elliptical optical aperture of 1100 x 730 mm, cut from a rolled plate of Al 6061-T651, the current baseline for Ariel telescope mirrors and supporting structure; 2. 6 aluminum samples, shaped as disks 6 mm thick 25 mm in diameter, obtained from the same plate from which the PTM substrate had been cut (Figure 2 shows one of the samples being held for visual inspection before the coating run); 3. 2 sets of glass samples measuring 25 mm and 48 mm in diameter respectively to serve as reference for spectral reflectivity and for the profilometry measurements.
Figure 1.Picture of the PTM mirror mounted on its transport and handling trolley before coating (courtesy of CILAS). ![00157_PSISDG11852_118524L_page_4_1.jpg](ContentImages/Proceedings/11852/118524L/FigureImages/00157_PSISDG11852_118524L_page_4_1.jpg) Figure 2.Picture of an aluminum sample used for the qualification during a visual inspection before being coated (courtesy of CILAS). ![00157_PSISDG11852_118524L_page_4_2.jpg](ContentImages/Proceedings/11852/118524L/FigureImages/00157_PSISDG11852_118524L_page_4_2.jpg) The roughness of the optical surface on the aluminum samples was measured with a Taylor Hobson CCI White Light Interferometer with magnifications 10x and 50x. All samples measured roughness was within the 10 nm RMS specification. The surface roughness of the PTM, measured at 10 different locations on its optical surface, was instead in the range 21.5–26.9 nm RMS. The PTM and aluminum samples had been manufactured by MediaLario§. 2.2Coating ProcessThe coating process used by CILAS for this batch is based on physical vapor deposition. The items to be coated are laid on a tray that slides inside a large magnetron sputtering chamber, and moved back and forth beneath a set of cathodes, to minimize deposition inhomogeneities9. The process is suited to optical substrates up to 2 m by 2 m of footprint and 0.4 m of thickness10. The protected silver coating employed for the study consists of three layers: a NiCr adhesion layer of less than 10 nm of thickness, the silver layer, and a dielectric capping and protection layer. The process had already been qualified on aluminum samples and produces a coating layer measuring on average 350 nm of thickness, with 10% uniformity. The layout of the items on the coating tray is shown in Figure 3. Figure 3.Layout of the items to be coated on the tray of the coating chamber. The blue arrow indicates the direction of insertion into the chamber. ![00157_PSISDG11852_118524L_page_5_1.jpg](ContentImages/Proceedings/11852/118524L/FigureImages/00157_PSISDG11852_118524L_page_5_1.jpg) 3.VERIFICATION METHODSThe tests described in this paper have the purpose of verifying that the performance and durability of the protected silver coating deposited on the PTM are consistent with the results obtained during the qualification phase 8. Four of the witness samples deposited together with the PTM were therefore subjected to a series of humidity, temperature, cleaning, abrasion and adhesion tests, evaluated by visual inspection and assessment of the variation of relative spectral reflectivity measurements taken before and after the set of tests. Additionally, the coating thickness was measured on one of the glass samples, and the durability of the coating on the PTM was assessed through adhesion testing. The following paragraphs describe the details of the verification methods employed. 3.1Visual InspectionVisual inspection was performed at CILAS on the optical area of each sample according to ISO standard 9211-4:201211. Inspection of the PTM was performed both by CILAS and MediaLario. 3.2Relative Reflectivity MeasurementsRelative reflectivity measurements were performed at CILAS with a Perkin-Elmer Lambda 950 spectrophotometer with a reflectometry accessory in the waveband 500 nm–2500 nm and with an accuracy of ±0.6% from 500 nm to 890 nm and ±1% above 890 nm. 3.3Humidity TestThe test was realized at CILAS according to ISO 9211-3:200812 Test #5 (damp heat). The samples were exposed to a 90% humidity environment at 55°C (+/-3°C) for 24 hours with a maximum temperature slope of 2°C/minute. No condensation was observed on the coated surfaces during the test. 3.4Temperature Cycling TestThe samples were subjected to 30 cycles between -40°C and 70°C with a maximum temperature slope of 2°C/minute and a dwell time of 15 minutes. The test was performed at CILAS. 3.5Cleaning TestThe test was performed at CILAS applying their standard cleaning procedure based on ethanol and acetone solutions, using an optical wipe. The test was repeated 5 times. 3.6Abrasion TestTest realized at CILAS on one sample, according to ISO 9211-4:201211, Test Method 01, Severity Level 01. 3.7Adhesion TestAdhesion tests were performed following ISO Standard 9211-4, Method 02, Severity 0211. Tests on samples were performed at CILAS with a cellophane tape, while the test on the optical surface of the PTM was performed at MediaLario using Kapton® tape strips. 4.TEST RESULTS4.1Environmental and Mechanical TestsOne aluminum sample was subjected to the whole sequence of chemical/mechanical tests (cleanability, abrasion and adhesion), while three other samples underwent the environmental set of tests (humidity and temperature cycling) and later the adhesion test. The two remaining aluminum samples have been kept as references for aging. Results were satisfactory and in line with the outcomes from the coating qualification phase: no discernible signs of coating degradation nor delamination were apparent. Reflectivity measurements did not highlight any change in performance either, as described in paragraph 4.2. Adhesion tests on the coated PTM were performed on two separate areas of the mirror, and were also successful with no sign of coating degradation nor visually detectable traces of the coating on the tape strip (Figure 4). Figure 4.Adhesion test on the PTM mirror. On the left, the tape positioned perpendicular to the edge of the mirror right before lift-off. On the right, the sticky side of the tape after lift-off, showing no detached coating particles (pictures courtesy of MediaLario). ![00157_PSISDG11852_118524L_page_6_1.jpg](ContentImages/Proceedings/11852/118524L/FigureImages/00157_PSISDG11852_118524L_page_6_1.jpg) 4.2Reflectivity MeasurementsFigure 5 illustrates reflectivity measurements of the samples that underwent mechanical (#18, 19, 20) and cleaning (#16) tests. Variations between measurements of the same sample are within the accuracy of the measurement instrument. Figure 5.Reflectivity measurements of samples 16, 18, 19 and 20 before (“Pre” in the legend) and after (“Post” in the legend) the tests, showing no significant change. ![00157_PSISDG11852_118524L_page_7_1.jpg](ContentImages/Proceedings/11852/118524L/FigureImages/00157_PSISDG11852_118524L_page_7_1.jpg) 4.3ProfilometryGlass sample number 14 was partially covered with a mask during coating, and the depth of the resulting ridge was measured with a profilometer in two points. The resulting coating thicknesses were 342 nm and 345 nm, compatible with measurements taken during the qualification coating run at the same position in the coating chamber of 348 nm. 5.CONCLUSIONSFollowing the successful qualification of the selected protected silver coating for the aluminum mirrors of the Ariel telescope, a coating test run was performed on the full size demonstrator of the telescope primary mirror (PTM), together with 6 aluminum samples, to further confirm performance and durability of the coating. Results of adhesion, abrasion, cleaning, humidity and thermal cycling tests performed on the samples and verified by visual inspections and reflectivity measurements showed no alteration in appearance imputable to deterioration or delamination of the coating, nor a degradation in optical performance in the waveband 500–2500 nm. Adhesion tests performed on the optical surface of the PTM further confirmed the durability of the coating. These results were considered satisfactory and led to a successful termination of the coating qualification campaign. Further measurements on the samples will be repeated periodically to assess possible aging deterioration. 6.ACKNOWLEDGEMENTSThis activity has been realized under the Italian Space Agency (ASI) contract with the National Institute for Astrophysics (INAF) n. 2018-22-HH.0, and is partly funded under the ESA contract with Centre Spatial de Liège, Belgium (CSL) and INAF n. 4000126124/18/NL/BW. REFERENCESDa Deppo, V., Middleton, K., Focardi, M., Morgante, G., Claudi, R., Pace, E., Grella, S., Ficai Veltroni, I. and Micela, G.,
“The afocal telescope optical design and tolerance analysis for the ESA ARIEL mission,”
in Proc. SPIE 10590, International Optical Design Conference 2017,
(2017). Google Scholar
Puig, L., Pilbratt, G., Heske, A., Escudero, I., Crouzet, P.-E., de Vogeleer, B., Symonds, K., Kohley, R., Drossart, P., Eccleston, P., Hartogh, P., Leconte, J., Micela, G., Ollivier, M., Tinetti, G., Turrini, D., Vandenbussche, B. and Wolkenberg, P.,
“The Phase A study of the ESA M4 mission candidate ARIEL,”
Exp Astron, 46
(1), 211
–239
(2018). https://doi.org/10.1007/s10686-018-9604-3 Google Scholar
Kroes, G., Oudenhuysen, A., Meijers, M. and Pel, J.-W.,
“MIRI-JWST spectrometer main optics opto-mechanical design and prototyping,”
in Proc. SPIE 5877, Optomechanics 2005,
58770P
(2005). Google Scholar
Da Deppo, V., Gianluca, M., Emanuele, P., Middleton, K. and Paul, E.,
“ARIEL Telescope Material Trade-Off,”
Technical Paper ARIEL-INAF-PL-TN-004, 10,
(2017). Google Scholar
Boccas, M., Vucina, T., Araya, C., Vera, E. and Ahhee, C.,
“Coating the 8-m Gemini telescopes with protected silver,”
in Proc. SPIE 5494, Optical Fabrication, Metrology, and Material Advancements for Telescopes,
(2004). https://doi.org/10.1117/12.548809 Google Scholar
Sheikh, D. A.,
“Improved silver mirror coating for ground and space-based astronomy,”
in Proc. SPIE 9912, Advances in Optical and Mechanical Technologies for Telescopes and Instrumentation II,
(2016). Google Scholar
Schürmann, M., Jobst, P. J., Stenzel, O., Wilbrandt, S., Szeghalmi, A., Bingel, A., Munzert, P., Kaiser, N. and Schwinde, S.,
“High-reflective coatings for ground and space based applications,”
in SPIE 10563, International Conference on Space Optics — ICSO 2014,
(2017). Google Scholar
Chioetto, P., Zuppella, P., Da Deppo, V., Pace, E., Morgante, G., Terenzi, L., Brienza, D., Missaglia, N., Bianucci, G., Spinelli, S. M., Guerriero, E., Rossi, M., Bondet, C., Chauveau, G., Porta, C., Grezes-Besset, C., Malaguti, G. and Micela, G.,
“The primary mirror of the Ariel mission: cryotesting of aluminum mirror samples with protected silver coating,”
in Proc. SPIE 11451, Advances in Optical and Mechanical Technologies for Telescopes and Instrumentation IV,
(2020). Google Scholar
Savin de Larclause, I., Valette, N., Chauveau, G., Grèzes-Besset, C., Costes, V., Gasc, K. and Lemarquis, F.,
“PACA2m magnetron sputtering silver coating: a solution for very big mirror dimensions,”
in Proc. SPIE 10563, International Conference on Space Optics — ICSO 2014,
1056308
(2018). Google Scholar
Grèzes-Besset, C., Valette, N., Chauveau, G., Castelnau, M., Mathieu, K., Tatat, M. and Lemarquis, F.,
“High performance silver coating with PACA2M magnetron sputtering,”
in Proc. SPIE 11180, International Conference on Space Optics — ICSO 2018,
1118083
(2019). Google Scholar
International Organization for Standardization.,
“International Standard 9211-4: Optics and photonics — Optical coatings — Part 4: Specific test methods,”
(2012). Google Scholar
International Organization for Standardization.,
“International Standard 9211-3: Optics and photonics — Optical coatings — Part 3: Environmental durability,”
(2018). Google Scholar
|