Fatigue of polycrystalline silicon films with thin surface oxides

O. N. Pierron; C. L. Muhlstein

doi:10.1117/12.646468

5 January 2006 Fatigue of polycrystalline silicon films with thin surface oxides

O. N. Pierron, C. L. Muhlstein

Proceedings Volume 6111, Reliability, Packaging, Testing, and Characterization of MEMS/MOEMS V; 611106 (2006) https://doi.org/10.1117/12.646468
Event: MOEMS-MEMS 2006 Micro and Nanofabrication, 2006, San Jose, California, United States

Abstract

The performance of structural films under cyclic loading conditions is a critical consideration when designing microelectromechanical systems (MEMS) based on silicon structural films. Empirical and theoretical studies have shown that silicon films are susceptible to fatigue at room temperature, but the underlying mechanistic origin is still an active topic of debate. This study characterized the fatigue behavior of electrostatically-actuated, n⁺-type, 2 μm thick polycrystalline silicon films with a thin native oxide. Electrostatically actuated resonators (natural frequency, f₀~ 40 kHz) were used to evaluate the stress-life fatigue behavior of the films in 30°C, 50% relative humidity (R.H.) air. These tests revealed delayed failure with increasing fatigue lives (up to 10¹¹ cycles) for decreasing stress amplitudes (down to 2.5 GPa). Long fatigue lives were associated with larger decreases in f₀ and very smooth failure origins that encompassed several grains. These findings are consistent with cyclic degradation of silicon films occurring within a surface reaction layer that forms upon exposure to the service environment and that evolves during fatigue loading.

Citation Download Citation

O. N. Pierron and C. L. Muhlstein "Fatigue of polycrystalline silicon films with thin surface oxides", Proc. SPIE 6111, Reliability, Packaging, Testing, and Characterization of MEMS/MOEMS V, 611106 (5 January 2006); https://doi.org/10.1117/12.646468

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available