We demonstrated a middle-wavelength infrared (MWIR) graphene photodetector using the photogating effect. This effect was induced by photosensitizers situated around a graphene channel that coupled incident light and generated a large electrical charge. The graphene-based MWIR photodetector consisted of a top graphene channel, source–drain electrodes, an insulator layer, and a photosensitizer, and its photoresponse characteristics were determined by current measurements. Irradiation of the graphene channel of the vacuum cooled device by an MWIR laser generated a clear photoresponse, as evidenced by modulation of the output current during irradiation. The MWIR photoresponse with the photogating effect was 100 times greater than that obtained from conventional graphene photodetectors without the photogating effect. The device maintained its MWIR photoresponse at temperatures up to 150 K. The effect of the graphene channel size on the responsivity was evaluated to assess the feasibility of reducing the photodetector area, and decreasing the channel area from 100 to 25 μm2 improved the responsivity from 61.7 to 321.0 AW − 1. The results obtained in our study will contribute to the development of high-performance graphene-based IR imaging sensors. |
1.IntroductionInfrared (IR) imaging has been employed in a wide range of applications.1 The 3- to spectral band corresponding to the middle-wavelength IR (MWIR) region is especially important with regard to IR imaging, because this band is associated with commonly encountered temperatures. The 8- to band corresponding to the long wavelength IR (LWIR) region is also important. The tracking of hot bodies (), aerial and satellite reconnaissance, and gas detection2 using the MWIR region are currently performed with either thermal or quantum photodetectors. Thermal photodetectors respond to IR radiation by converting temperature changes into electronic signals and have the advantages of being inexpensive and operable at room temperature. However, the responsivity and response time of these devices are inferior to those of quantum detectors, which respond to IR light via a photoelectric conversion process. However, although quantum detectors provide superior responsivity, they contain toxic semiconductor materials such as mercury–cadmium–telluride. Therefore, there is a demand for low-cost, nontoxic, high-responsivity photomaterials so as to obtain the advantages of both types of IR photodetectors. Such materials would expand the range of applications of these devices. Graphene has remarkable optoelectronic properties and thus could represent a means of improving photodetectors. As a result of its Dirac-cone band structure,3,4 graphene exhibits broadband light absorption,5–7 a rapid response,8–12 gate-tunable plasmons,13,14 and a strong nonlinear optical response.15–17 In addition, graphene can be obtained at low cost through a nontoxic synthetic route, unlike quantum photomaterials.18–20 Therefore, graphene photodetectors are expected to expand the range of IR applications due to these advantages. However, since graphene has a low light-absorption value of ,21 a method is required to enhance the responsivity, such as the use of plasmonic antennas,22 optical waveguides,23 or photocarrier injection.24 We have previously investigated various techniques for this purpose, including the use of p–n junctions,25 plasmonic metamaterial absorbers,26–28 and the photogating effect.29–34 Here, we report a detailed mechanism for the photogating effect that significantly improves the responsivity of graphene photodetectors operating in the MWIR spectral band. 2.Device Fabrication and AssessmentFigure 1(a) shows a schematic illustration of the graphene photodetector used in this work, which is based on the design of a graphene field effect transistor (FET).3,35 To produce this device, a p-type indium antimonide (InSb) substrate with a 260-nm-thick tetraethyl orthosilicate (TEOS) layer was initially prepared. Subsequently, source–drain electrodes made of 10-nm-thick Cr and 30-nm-thick Au layers were sputter deposited on the TEOS layer. The graphene was fabricated by chemical vapor deposition and then transferred onto the substrate on which the source–drain electrodes had been produced using a conventional graphene-transfer method.36,37 Following this, a -wide and -long graphene channel was formed using a combination of photolithography and etching. Figure 1(b) presents the Raman spectrum obtained from this channel using a 512-nm excitation laser. The spectrum exhibits typical characteristics of graphene, including a peak at and a peak at , corresponding to the bond stretching and second-order breathing modes of carbon atoms, respectively.38–40 Therefore, this spectrum confirms that a monolayer graphene channel was successfully fabricated. The responsivity of each graphene photodetector made during this study was investigated by electrical current measurements. In these trials, the device was positioned in a cooled vacuum probe system after which a source–drain voltage () of 1.0 V and a back-gate voltage () between and 40 V were applied using a device analyzer. was applied to the back side of the substrate. Figure 2 plots the source–drain current () as a function of for this device obtained at 77 K. Prior to these measurements, the Dirac point for each photodetector was tuned around a of by vacuum calcination at 423 K. The graphene channel was exposed to light emitted from a diode fiber laser or to 4.6-, 8.0-, or radiation from a quantum cascade laser. The photoresponse was calculated based on the extent of modulation between illuminated and dark conditions (photocurrent, ). The time-dependent current characteristics were measured with a dwell time of 80 ms and a 0.1-fA measurement resolution. 3.Results and Discussion3.1.Photogating Modulation in MWIR PhotoresponseThe MWIR photoresponse of the graphene photodetector was initially investigated. Figure 3(a) shows the response of the device using a of 1.0 V and a of 0 V at 50 K. The device was exposed to the laser in conjunction with a 2.0-s irradiation cycle (0.8 s on, 1.2 s off) and exhibited a definite photoresponse by generating an of during irradiation. Figure 3(b) shows the back-gate current () during laser light irradiation. The photoresponse was associated with variations in , which in turn were modulated by the electrical charge in the InSb photosensitizer. The effect of on was also investigated to further analyze the photogating effect. Figure 4(a) shows the experimentally determined gating responses under dark and illuminated conditions. The lowest was obtained at a of , which corresponds to the Dirac point for graphene. Figures 4(b)–4(d) present magnified views of the gating responses around values of 0 and 23.5 V, and Fig. 4(b) demonstrates an 87.0-mV change in the response at a of 0 V. In contrast, Figs. 4(c) and 4(d) show only a slight variation of 0.5 mV. The photogating effect is primarily attributed to the behavior of photocarriers in the InSb photosensitizer. When a negative is applied to such a device, electron–hole pairs become separated in the p-doped InSb substrate, and the photoelectrons accumulate at the TEOS/InSb boundary. This surplus of electrons in the boundary region modulates the built-in electric field, which leads to the photogating effect. The results clearly indicate that the photogating effect enhances the photoresponse of the graphene by a factor of more than 100 compared with the inherent photoresponses of graphene obtained from photovoltaic,10,25,41 bolometric,35 and photothermoelectric effects.42–44 The photogating effect is achieved by modulating via photocarriers generated in the InSb substrate. The sequence of events by which the photoresponse of the device appears in conjunction with the photogating effect can be summarized as follows. First, during light irradiation at wavelengths shorter than the cutoff wavelength of the InSb substrate, electron–hole pairs (photocarriers) are generated in the InSb. These photoelectrons/holes are subsequently separated via the application of . Second, the photoelectrons accumulate in the depletion layer at the TEOS/InSb boundary as a consequence of ,29 and is modulated by the internal electric field generated by the accumulated photoelectrons. Third, the field effect in the graphene is changed by the modulation of . Specifically, variations in change the surface charge density of the graphene, and the corresponding change in the electrical signal from the graphene channel is detected as the photoresponse. 3.2.Wavelength DependenceThe wavelength dependence of the device performance was also investigated, and Fig. 5 shows the photoresponse of the device during pulsed laser light irradiation at 0.6, 1.6, 8.0, and . The device evidently exhibited a photoresponse with modulation under irradiation at 0.6 and . However, the photoresponse of the device was found to decrease significantly at longer wavelengths such that, as shown in Figs. 5(c) and 5(d); no photoresponse was obtained during irradiation in the LWIR region at 8.0 and . The photoresponse data obtained from a Si-based graphene FET were compared with those from an InSb-based graphene FET with both p-doped photosensitizers. A clear photoresponse was confirmed under irradiation at wavelengths shorter than the cutoff wavelength of the photosensitizer for both devices. Figure 6 presents the visible light photoresponse of the Si graphene FET and the MWIR photoresponse of the InSb graphene FET. The Si-based device produced a photoresponse under visible light irradiation [Figs. 6(a) and 6(b)], and the photoresponse characteristics together with the distinct back-gate voltage profile indicate the exact same behavior as that for the InSb-based graphene FET under MWIR irradiation [Figs. 6(c) and 6(d)]. At wavelengths longer than the bandgap wavelength, the photoresponses of both devices were decreased significantly. The MWIR and LWIR photoresponses of the Si-based graphene FET were especially weak, in the vicinity of only several mA/W. We also ascertained that the InSb-based graphene FET did not exhibit a photoresponse under LWIR light irradiation. In addition, generation of photocarriers in the photosensitizers under longer wavelength light was not evident, based on modulation of the gate current. Therefore, it can be concluded that the MWIR photoresponse of the InSb-based graphene FET was enhanced by the photogating effect. 3.3.Temperature DependenceThe effect of temperature on the MWIR photoresponse was assessed, and Fig. 7 shows the photoresponses obtained from the device at 150 and 200 K. At 150 K, the photogating effect was weakened by the generation of hot carriers, and so the inherent photoresponse of the graphene itself played the dominant role. At 200 K, was evidently not synchronized with the laser pulses. In addition, exhibited greater fluctuations in response to thermally generated carriers during pulsed irradiation compared with fluctuations at lower temperatures. Consequently, the photogating effect was weakened and an MWIR photoresponse could not be confirmed. At high temperatures, hot carriers would be expected to be generated in the InSb substrate as a consequence of thermal excitation, leading to changes in due to the varying concentrations of photocarriers. 3.4.Device-Size DependenceThe effect of the graphene channel dimensions on the MWIR photoresponse was also evaluated. Figure 8 plots the photoresponses of two devices having different channel aspect ratios but the same total channel area of . The photoresponse is seen to increase from to upon increasing the ratio of the width () of the channel to its length () of gap between electrodes. The devices operate under the same principles as metal–oxide–semiconductor FETs, so changing the ratio causes a resistance change in the graphene channel. The effects of the graphene channel shape on the MWIR photoresponse were evaluated in more detail, and Fig. 9 plots for ratios from 0.25 to 8.00. It is noteworthy that these values have been normalized with respect to the graphene field effect mobility (), because varied slightly even though the Dirac point for all devices was tuned to be about the same at 0 to 10 V. Assigning a value of 1 to for an aspect ratio of 8, values of 0.04, 0.08, 0.17, 0.26, 0.49, and 0.66 were obtained for aspect ratios of 0.25, 0.5, 1, 2, 4, and 6, respectively. It is evident that the resulting plot describes an almost linear correlation between and the aspect ratio of the channel. This line can be fit using the exponential expression shown in the figure. The results indicate that the MWIR photoresponse was affected by the shape of the graphene channel but not by the irradiated area or the total incident light power. Figure 10(a) shows the MWIR responses of devices with channels having a fixed width of and lengths of 5, 10, 15, or . The responsivity was calculated from the photocurrent, the incident light intensity of , and the irradiated surface area, which is determined by the graphene channel size and the photocarrier diffusion distance in the InSb photosensitizers. The responsivity increases significantly with decreasing channel area, with values of 61.7, 68.1, 159.1, and corresponding to areas of 100, 75, 50, and , respectively. In general, the responsivity of a conventional photodetector is proportional to the irradiated area, because incident light energy is directly converted to a signal current/bias. In contrast, the photoresponse of a graphene photodetector using the photogating effect is not based on the direct collection of photoelectrons/holes from the photosensitizers but on modulation of the field effect around the graphene channel. A sufficiently strong field-effect modulation can be obtained via the localized accumulation of photoelectrons/holes in a depletion layer. Therefore, expansion of the irradiated area is not required in order to enhance the responsivity of such devices. A decrease in the graphene channel area leads to a change in the aspect ratio, which causes an increase in the photocurrent. The results of this work demonstrate that increasing the aspect ratio of the graphene channel decreases the device area and also improves the responsivity. 4.ConclusionIn conclusion, high-responsivity graphene photodetectors that operate in the MWIR spectral band based on the photogating effect were demonstrated. These devices consisted of a top graphene channel, source–drain electrodes, an insulator layer, and photosensitizers. An analysis of the effects of the irradiation wavelength and the photosensitizer on the photoresponse demonstrated that the photogating effect was induced by photosensitizers located around the graphene channel, as these materials couple incident light to generate a significant electrical charge. The MWIR photoresponse obtained in conjunction with the photogating effect was 2 orders of magnitude greater than that observed for conventional graphene photodetectors without this effect. The MWIR photoresponse was also found to be maintained at temperatures up to 150 K. The dimensions of the graphene channel were found to affect the photoresponse, showing that additional increases in photoresponse are possible via decreases in the device area. The results of this work are expected to assist in the future design and development of high-performance graphene-based IR imaging sensors. AcknowledgmentsThis work was partially supported by the Innovative Science and Technology Initiative for Security, ATLA, Japan. ReferencesM. Vollmer and K.-P. Mollmann, Infrared Thermal Imaging: Fundamentals, Research and Applications, Wiley-VCH, Weinheim, Germany
(2010). Google Scholar
H. Budzier and G. Gerlach, Thermal Infrared Sensors: Theory, Optimisation and Practice, John Wiley & Sons, Ltd., West Sussex
(2011). Google Scholar
K. S. Novoselov et al.,
“Electric field effect in atomically thin carbon films,”
Science, 306
(5696), 666
–669
(2004). https://doi.org/10.1126/science.1102896 SCIEAS 0036-8075 Google Scholar
K. S. Novoselov et al.,
“Two-dimensional gas of massless Dirac fermions in graphene,”
Nature, 438
(7065), 197
–200
(2005). https://doi.org/10.1038/nature04233 Google Scholar
G. Pirruccio et al.,
“Coherent and broadband enhanced optical absorption in graphene,”
ACS Nano, 7
(6), 4810
–4817
(2013). https://doi.org/10.1021/nn4012253 ANCAC3 1936-0851 Google Scholar
S. Ogawa et al.,
“Broadband photoresponse of graphene photodetector from visible to long-wavelength infrared wavelengths,”
Opt. Eng., 58
(5), 057106
(2019). https://doi.org/10.1117/1.OE.58.5.057106 Google Scholar
T. Wu, Y. Luo and L. Wei,
“Mid-infrared sensing of molecular vibrational modes with tunable graphene plasmons,”
Opt. Lett., 42
(11), 2066
–2069
(2017). https://doi.org/10.1364/OL.42.002066 OPLEDP 0146-9592 Google Scholar
F. Xia et al.,
“Ultrafast graphene photodetector,”
Nat. Nanotechnol., 4
(12), 839
–843
(2009). https://doi.org/10.1038/nnano.2009.292 NNAABX 1748-3387 Google Scholar
Y. M. Lin et al.,
“100-GHz transistors from wafer-scale epitaxial graphene,”
Science, 327
(5966), 662
–662
(2010). https://doi.org/10.1126/science.1184289 SCIEAS 0036-8075 Google Scholar
T. Mueller, F. Xia and P. Avouris,
“Graphene photodetectors for high-speed optical communications,”
Nat. Photonics, 4
(5), 297
–301
(2010). https://doi.org/10.1038/nphoton.2010.40 NPAHBY 1749-4885 Google Scholar
X. Gan et al.,
“Chip-integrated ultrafast graphene photodetector with high responsivity,”
Nat. Photonics, 7
(11), 883
–887
(2013). https://doi.org/10.1038/nphoton.2013.253 NPAHBY 1749-4885 Google Scholar
X. Guo et al.,
“High-performance graphene photodetector using interfacial gating,”
Optica, 3
(10), 1066
–1070
(2016). https://doi.org/10.1364/OPTICA.3.001066 Google Scholar
J. Chen et al.,
“Optical nano-imaging of gate-tunable graphene plasmons,”
Nature, 487
(7405), 77
–81
(2012). https://doi.org/10.1038/nature11254 Google Scholar
B. Yao et al.,
“Broadband gate-tunable terahertz plasmons in graphene heterostructures,”
Nat. Photonics, 12
(1), 22
–28
(2018). https://doi.org/10.1038/s41566-017-0054-7 NPAHBY 1749-4885 Google Scholar
E. Hendry et al.,
“Coherent nonlinear optical response of graphene,”
Phys. Rev. Lett., 105
(9), 097401
(2010). https://doi.org/10.1103/PhysRevLett.105.097401 PRLTAO 0031-9007 Google Scholar
S. Shareef, Y. S. Ang and C. Zhang,
“Room-temperature strong terahertz photon mixing in graphene,”
J. Opt. Soc. Am. B, 29
(3), 274
–279
(2012). https://doi.org/10.1364/JOSAB.29.000274 JOBPDE 0740-3224 Google Scholar
K. J. A. Ooi et al.,
“Electronic scattering of graphene plasmons in the terahertz nonlinear regime,”
IEEE J. Sel. Top. Quantum Electron., 23
(4), 1
–6
(2017). https://doi.org/10.1109/JSTQE.2016.2615946 IJSQEN 1077-260X Google Scholar
L. Gao, J. R. Guest and N. P. Guisinger,
“Epitaxial graphene on Cu(111),”
Nano Lett., 10
(9), 3512
–3516
(2010). https://doi.org/10.1021/nl1016706 NALEFD 1530-6984 Google Scholar
D. Ding et al.,
“Behavior and role of superficial oxygen in Cu for the growth of large single-crystalline graphene,”
Appl. Surf. Sci., 408 142
–149
(2017). https://doi.org/10.1016/j.apsusc.2017.02.250 ASUSEE 0169-4332 Google Scholar
X. Li et al.,
“Transfer of large-area graphene films for high-performance transparent conductive electrodes,”
Nano Lett., 9
(12), 4359
–4363
(2009). https://doi.org/10.1021/nl902623y NALEFD 1530-6984 Google Scholar
R. R. Nair et al.,
“Fine structure constant defines visual transparency of graphene,”
Science, 320
(5881), 1308
(2008). https://doi.org/10.1126/science.1156965 SCIEAS 0036-8075 Google Scholar
Y. Yao et al.,
“High-responsivity mid-infrared graphene detectors with antenna-enhanced photocarrier generation and collection,”
Nano Lett., 14
(7), 3749
–3754
(2014). https://doi.org/10.1021/nl500602n NALEFD 1530-6984 Google Scholar
J. Wang et al.,
“High-responsivity graphene-on-silicon slot waveguide photodetectors,”
Nanoscale, 8
(27), 13206
–13211
(2016). https://doi.org/10.1039/C6NR03122F NANOHL 2040-3364 Google Scholar
G. Konstantatos et al.,
“Hybrid graphene–quantum dot phototransistors with ultrahigh gain,”
Nat. Nanotechnol., 7 363
–368
(2012). https://doi.org/10.1038/nnano.2012.60 NNAABX 1748-3387 Google Scholar
M. Shimatani et al.,
“Photocurrent enhancement of graphene phototransistors using p-n junction formed by conventional photolithography process,”
Jpn. J. Appl. Phys., 55
(11), 110307
(2016). https://doi.org/10.7567/JJAP.55.110307 Google Scholar
S. Ogawa, D. Fujisawa and M. Ueno,
“Effect of graphene on plasmonic metasurfaces at infrared wavelengths,”
AIP Adv., 3
(11), 112127
(2013). https://doi.org/10.1063/1.4834976 AAIDBI 2158-3226 Google Scholar
S. Ogawa et al.,
“Graphene on metal–insulator–metal-based plasmonic metamaterials at infrared wavelengths,”
Opt. Express, 26
(5), 5665
–5674
(2018). https://doi.org/10.1364/OE.26.005665 OPEXFF 1094-4087 Google Scholar
M. Shimatani et al.,
“Multispectral graphene infrared photodetectors using plasmonic metasurfaces,”
Proc. SPIE, 11002 1100224
(2019). https://doi.org/10.1117/12.2518399 PSISDG 0277-786X Google Scholar
M. Shimatani et al.,
“Giant Dirac point shift of graphene phototransistors by doped silicon substrate current,”
AIP Adv., 6
(3), 035113
(2016). https://doi.org/10.1063/1.4944622 AAIDBI 2158-3226 Google Scholar
S. Fukushima et al.,
“High responsivity middle-wavelength infrared graphene photodetectors using photo-gating,”
Appl. Phys. Lett., 113
(6), 061102
(2018). https://doi.org/10.1063/1.5039771 APPLAB 0003-6951 Google Scholar
M. Shimatani et al.,
“Enhanced photogating via pyroelectric effect induced by insulator layer for high-responsivity long-wavelength infrared graphene-based photodetectors operating at room temperature,”
Appl. Phys. Express, 12
(2), 025001
(2019). https://doi.org/10.7567/1882-0786/aaf90a APEPC4 1882-0778 Google Scholar
S. Fukushima et al.,
“High-responsivity graphene infrared photodetectors using photo-gating effect,”
Proc. SPIE, 11002 1100223
(2019). https://doi.org/10.1117/12.2518396 PSISDG 0277-786X Google Scholar
S. Fukushima et al.,
“Low dark current and high-responsivity graphene mid-infrared photodetectors using amplification of injected photo-carriers by photo-gating,”
Opt. Lett., 44
(10), 2598
–2601
(2019). https://doi.org/10.1364/OL.44.002598 OPLEDP 0146-9592 Google Scholar
M. Shimatani et al.,
“High-responsivity turbostratic stacked graphene photodetectors using enhanced photogating,”
Appl. Phys. Express, 12
(12), 122010
(2019). https://doi.org/10.7567/1882-0786/ab5096 APEPC4 1882-0778 Google Scholar
J. B. Oostinga et al.,
“Gate-induced insulating state in bilayer graphene devices,”
Nat. Mater., 7
(2), 151
–157
(2008). https://doi.org/10.1038/nmat2082 NMAACR 1476-1122 Google Scholar
J. W. Suk et al.,
“Transfer of CVD-grown monolayer graphene onto arbitrary substrates,”
ACS Nano, 5
(9), 6916
–6924
(2011). https://doi.org/10.1021/nn201207c ANCAC3 1936-0851 Google Scholar
K. Uemura, T. Ikuta and K. Maehashi,
“Turbostratic stacked CVD graphene for high-performance devices,”
Jpn. J. Appl. Phys., 57
(3), 030311
(2018). https://doi.org/10.7567/JJAP.57.030311 Google Scholar
A. C. Ferrari et al.,
“Raman spectrum of graphene and graphene layers,”
Phys. Rev. Lett., 97
(18), 187401
(2006). https://doi.org/10.1103/PhysRevLett.97.187401 PRLTAO 0031-9007 Google Scholar
J.-S. Hwang et al.,
“Imaging layer number and stacking order through formulating Raman fingerprints obtained from hexagonal single crystals of few layer graphene,”
Nanotechnology, 24
(1), 015702
(2012). https://doi.org/10.1088/0957-4484/24/1/015702 NNOTER 0957-4484 Google Scholar
A. Reina et al.,
“Transferring and identification of single- and few-layer graphene on arbitrary substrates,”
J. Phys. Chem. C, 112
(46), 17741
–17744
(2008). https://doi.org/10.1021/jp807380s JPCCCK 1932-7447 Google Scholar
T. J. Echtermeyer et al.,
“Strong plasmonic enhancement of photovoltage in graphene,”
Nat. Commun., 2
(1), 458
(2011). https://doi.org/10.1038/ncomms1464 NCAOBW 2041-1723 Google Scholar
J. C. Song et al.,
“Hot carrier transport and photocurrent response in graphene,”
Nano Lett., 11
(11), 4688
–4692
(2011). https://doi.org/10.1021/nl202318u NALEFD 1530-6984 Google Scholar
N. M. Gabor et al.,
“Hot carrier-assisted intrinsic photoresponse in graphene,”
Science, 334
(6056), 648
–652
(2011). https://doi.org/10.1126/science.1211384 SCIEAS 0036-8075 Google Scholar
D. Sun et al.,
“Ultrafast hot-carrier-dominated photocurrent in graphene,”
Nat. Nanotechnol., 7
(2), 114
–118
(2012). https://doi.org/10.1038/nnano.2011.243 NNAABX 1748-3387 Google Scholar
|